Chemical Composition And The Quality Of Fused Cast AZS

Fused cast AZS block is the essential refractory material used in the demanding areas of glass furnaces. The quality of fused cast AZS can affect the quality and production of glass and the service life of the glass furnaces. The chemical composition of fused cast AZS is one of the key factors that determine the crystal structure and the properties.

Fused cast AZS block has many chemical and physical properties over other refractory materials, such as high temperature resistance, dense crystal structure, low porosity, high mechanical strength, good chemical stability, good corrosion resistance, good thermal stability(1200℃) and high exudation temperature of glass phase(>1400℃). Due to the features mentioned above, it is widely used in the glass industry.

It is important to select high quality raw materials and improve the purity of the raw materials. Any change of the chemical composition can change the crystal structure. Too much SiO2 can cause the formation of mullite and the decrease of glassy phase and corundum, which will destroy the crystal structure and make the structure loose. ZrO2 has the features of high temperature resistance, high mechanical strength, good corrosion resistance to glass and good chemical stability, but the drawback is its bad thermal stability at 1000-1200℃.

The corrosion resistance to glass of fused cast AZS is related to not only the content of ZrO2 but also its micro-structure. The denser its micro-structure, the better its corrosion resistance to glass. Too much ZrO2 will make its micro-structure loose and the baddeleyite will drop into the glass melt, which will cause glass defects such as stones, stripes and bubbles and reduce the service life of the glass furnaces. Therefore, its corrosion resistance to glass is not proportional to the content of ZrO2. Besides, with the increase of ZrO2, the melting temperature and viscosity of the glass melt also increases, which increases the difficulty of manufacturing and casting.

The content of Na2O and the impurities such as Fe2O3, TiO2, CaO, MgO will also affect the quality of fused cast AZS. Therefore, the stability of chemical composition is important for the quality of fused cast AZS and the service life of the glass furnaces. Sunrise offers high quality fused cast AZS block 33#, 36# and 41#.

Комментарии

Зарегистрируйтесь или войдите, чтобы добавить комментарий

Новые заметки пользователя

REFRACTORY — Это просто Вьюи блог

10

How To Judge The Quality Of Fire Clay Brick

Fire clay brick accounts for an important position in the refractory industry. The most important feature of fire clay brick is that the ...

10

How to select fused cast AZS block

Recently, with the development of furnace technology, more and more fused cast AZS block is used in the glass furnace. So, how to select ...

9

The size and specification requirements for hot stov...

Hot stove fire clay brick is made of refractory clay as the raw material. It is used in the hot stove, regenerator and partition walls. I...

9

The Use Of Silica Brick In The Glass Furnace

Since the silica brick has low price, high purity, high softening temperature under load, no pollution to glass liquid and good resistanc...

9

The Checker Work of Glass Furnaces

The checker work of glass furnaces is subjected to more serious corrosion than the crown and sidewall since all checker bricks are subjec...

8

Applications of fire clay bricks

Fire clay brick plays a versatile role in the many industries. Fire clay brick can be used in the metallurgical industry. Fire clay ma...